SPECIFICATION Supplier : Samsung electro-mechanics Product : Multi-layer Ceramic Capacitor Samsung P/N : CL32B106KLULNNF Description : CAP, 10, 35V, 10%, X7R, 1210 A. Samsung Part Number Series Size Dielectric Capacitance Capacitance tolerance Rated Voltage Thickness CL 32 B 106 K L U L N N F Samsung Multi-layer Ceramic Capacitor 1210 (inch code) L: 3.2 0.3 W: Thickness division Inner electrode Termination Plating Product Special Packaging X7R 10 10 % 35 V 1.8 0.2 mm mm 2.5 0.2 mm Low profile Ni Cu Sn 100% (Pb Free) Normal Reserved for future use Embossed Type,13"reel(4,000ea) B. Samsung Reliability Test and Judgement condition Performance Capacitance Tan (DF) Insulation Resistance Appearance Withstanding Voltage Temperature Characteristics Adhesive Strength of Termination Bending Strength Solderability Test condition Within specified tolerance 0.1 max. 110% 1.00.2Vrms More than 100Mohm Rated Voltage 60~120 sec. No abnormal exterior appearance No dielectric breakdown or mechanical breakdown X7R Visual inspection 250% of the rated voltage (From -55 to 125, Capacitance change should be within 15%) No peeling shall be occur on the 500gF, for 101 sec. terminal electrode Capacitance change : within 12.5% Bending to the limit (1mm) with 1.0mm/sec. More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Soldering heat Capacitance change : Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Performance Vibration Test Capacitance change : Tan , IR : initial spec. within 5% Test condition Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours 3 direction (x, y, z) within 12.5% With rated voltage Moisture Resistance Capacitance change : Tan : 0.125 max IR : More than 12.5* High Temperature Resistance Capacitance change : within 12.5% With 150% of the rated voltage Tan : 0.125 max Max. operating temperature IR : More than 25* 1000+48/-0 hours Capacitance change : within 7.5% 1 cycle condition Tan , IR : initial spec. Min. operating temperature Max. operating temperature Temperature Cycling 402, 90~95%RH, 500+12/-0 hours 5 cycles test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue. 25 25